High-quality glass fibre mesh with oiled paper for bridging and covering swelling substrates and for bridging cracks.Ideal for plastering over timber framing, wood and wooden beams, glass wool wall joints and similar.Suitable for all types of plaster!Width: 16, 20, 25, 33 cmRoll length: 50lfmTechnical information: Information sheet: Beam fabric with oiled paperDescription: For perfect beam lamination. Wooden beams, iron girders, insulating materials and small cracks in walls no longer have a direct connection to the plaster. Quick and easy application thanks to several width variants.Beam fabric with oiled paper impresses with its adaptability for professional use.Can be cut with a knife or scissors.No adhesion of oiled paper and glass fibre mesh due to foreign bodiesSize: Dimensions rolls 50 mExterior plaster mesh close-meshed 10 x 10mm blueWidths:16 cm mesh plus oiled paper 10 cm20 cm mesh with oiled paper 12.5 cm25 cm mesh with oiled paper 16 cm33 cm mesh with oiled paper 25 cm

Clay adhesive and reinforcing mortar for reinforcing layers on clay boards as well as wood fibre finishing and interior insulation boards. Clay adhesive and reinforcing mortar consists of clay and cellulose. This guarantees optimum workability, even with thin coats. With a compressive strength of 3.9 MPa, which is new for clay mortar, and an adhesive strength of 0.85 MPa, clay bonding and reinforcing mortar guarantees the strength of the entire construction. It is the basis for fine Claytec clay finishing plasters and YOSIMA. With good preparatory work, it can also be simply painted with the Clayfix clay coating system.Data sheet Application videoHow to useAdhesive and bonding mortar as a dry, fine-grained ready-mix for bonding lightweight building and interior insulation boards to various substrates, as a reinforcing mortar on clay building boards, clay-hemp boards, wood fibre insulation and wood fibre finishing boards and mineral foam boards.CompositionSand up to 1.0 mm, clay and loam, talc, perlite, plant fibres and cellulose.Delivery form, yield25 kg bags (makes 17 litres of mortar for 5 m2), 48 bags/pal.StorageCan be stored in a cool, dry place indefinitely.Mortar preparationThe 25 kg dry mix is gradually stirred into 8-9 litres of clean water using a drill (≥ 800 watts) or mixer and stirring paddle (Ø 125 mm). The amount of water added is slightly less for bonding mortar. Working consistency paste-like according to the desired application with a notched trowel or spatula.Work well again after 30 minutes resting time. The mortar is now ready to use.Plaster baseThe substrate must be stable, frost-free, dry, clean, free of salt, sufficiently rough and absorbent. Levelling coats of clay plaster mortar must be completely dry.The surface must be as level as necessary for the bonding described below. Small unevenness (small individual areas up to 5 cm in diameter and 3 mm deep) can be levelled with the adhesive. Larger imperfections must be filled with a suitable mortar and left to dry.ApplicationThe adhesive is applied to the back of the panels to be bonded using a notched trowel or spatula (8-10 mm notches). A thin layer of adhesive should be applied to the entire surface, including the grooves. The first board is applied immediately and pressed firmly onto the substrate; contact must be ensured over the entire surface.Uneven masonry and plaster surfaces are slightly pre-wetted and roughly levelled. The back-coated boards (see above) are pressed in wet-on-wet.Boards can be additionally mechanically fixed as required, e.g. on sloping ceilings and roofs, see corresponding board product sheets or worksheets.As a bonding filler for thick-layer plasters on insulation boards (e.g. for wall surface heating) and similar applications, the slightly stiffer mortar is applied in the same way using a notched trowel or spatula.For reinforcement layers, the 3 mm thick mortar is applied. It can also be sprayed on with a plastering machine; resting times are not necessary for this application. Reinforcement mesh is worked into the surface of the layer while it is still wet.HardeningThe curing time is 24-72 hours, depending on the drying possibilities and absorbency of the substrate. With additional mechanical panel fixing and subsequent thin-layer coating, work can continue immediately.Work samplesAdhesion to the substrate must always be checked with the respective board to be fixed using a sufficiently large working sample. Complaints not resulting from mixing errors at the factory are excluded.

Surface reinforcement for clay adhesive and reinforcing mortar and all clay plasters. It is tension-resistant, very fine and particularly easy to work with.Clay plasters worksheetApplicationAs surface reinforcement for clay plasters, HFD interior insulation, cladding made of clay building boards and wood fibre boards, cladding made of clay building boards, clay-hemp boards and wood fibre boards.TextureLeno fabric made of glass fibre yarn/roving, finished with polymer finish for scrims. Weight approx. 110g/m², warp/weft approx. 14/14 Fa per 10 cm, clear mesh size approx. 6 x 6 mm, made in Germany, alkali-resistant, shift-proofDelivery formRoll, width 100 cm, length 50 mStorageDry, airy and protected from direct sunlight for at least three years.Material requirementAs for m² plaster surface plus 10% to 20% reserve for offcuts and overlaps.ApplicationSurface reinforcement: The mesh is applied to the freshly applied, still plastic mortar and rubbed in with the felt board. The overlap in the joint area must be approx. 10 cm. (For cladding made of clay building boards, clay hemp boards and wood fibre finishing boards, the fabric is usually worked into the clay adhesive and reinforcing mortar over the entire surface).